Gẹgẹbi China ṣe dabaa ni kedere ibi-afẹde “erogba meji” ni Oṣu Kẹsan ọdun 2020, ile-iṣẹ fọtovoltaic ti fa akiyesi pupọ bi orisun agbara mimọ, ati polysilicon bi ohun elo aise fun iṣelọpọ fọtovoltaic, ibeere ọja ti pọ si ni ọdun kan.
aworan1
Polycrystalline silicon-chilly hydrogenation bed riakito iṣelọpọ nigbagbogbo nlo irin UNS N08120 kan. Irin yii jẹ ohun elo ti o lagbara -soluble -sooro ooru -sooro alloy pẹlu kikankikan otutu giga giga, anti-carbonate ti o dara ati awọn agbara vulcanization.

Idagbasoke awọn ohun elo alurinmorin ti o le ṣee lo fun ohun elo iṣelọpọ polysilicon jẹ pataki nla lati ṣaṣeyọri ibi-afẹde ti “erogba meji”.

Ni idahun si awọn abuda alurinmorin ti irin UNS N08120, elekiturodu GEN-CM2 ti o dagbasoke nipasẹ ile-iṣẹ wa ni iṣẹ iwọn otutu to gaju to dara julọ. Awọn ipata resistance le baramu awọn alurinmorin ti awọn obi ohun elo.
1.Introduction to Gen-CM2 materialization iṣẹ ati awọn abuda ọja

Oruko

Standard

Iwa

GEN-CM2

GB/T 13814

Eni6002

Aws A5.11

ENiCrMo-2

1. Ni-CR-MO ni alloys, fi kan kekere iye ti W, CO, ati be be lo.

2. Melving irin ipata resistance, yara otutu, ga otutu darí išẹ ati kiraki resistance

3. Dara fun alurinmorin ti nickel -chromium -molybdenum alloys pẹlu ooru resistance awọn ibeere bi UNS N06002 ati N08120

Gen-CM2 yo irin darí išẹ aṣoju iye

Idanwo iwọn otutu

Yield agbara(Mpa)

Tensile agbara

(Mpa)

Eoṣuwọn itesiwaju

(%)

Bipari

Iwọn otutu yara

504

723

36.0

nudulu atunse, pada atunse tóótun

600

300

-

39.5

-

Gen-CM2 yo irin paati aṣoju iye

kemikali tiwqn(wt%)

C

Mn

Si

Cr

Ni

Mo

Fe

Co

W

0.096

0.68

0.36

22.2

46.1

9.7

19.3

1.06

0.42

2.Gen-CM2 alapin igun alurinmorin, atunse ati ibajẹ awọn aworan ayẹwo
aworan2
aworan3
aworan4
Gen-CM2 atunse ati ayẹwo ibajẹ

3.Ọja ti nfihan
aworan5
Awọn ila alurinmorin jara ti o da lori nickel wa ti lo ni awọn iṣẹ ṣiṣe alurinmorin pẹlu iṣẹ iduroṣinṣin ati igbẹkẹle. Awọn ọja elekiturodu alurinmorin Gen-CM2 ti jẹ apẹẹrẹ fun idanwo, eyiti o ti gba iyin apapọ.

Kaabọ awọn alabara lati beere ati ra!