AWS E8015-G iru ọwọ alurinmorin elekiturodu fun ooru-sooro irin ni o dara fun ga otutu ati ki o ga titẹ ileru opo gigun ti agbara ibudo, ga otutu sintetiki ẹrọ kemikali, epo refining ẹrọ, ati be be lo pẹlu awọn iwọn otutu ṣiṣẹ labẹ 540 ℃, gẹgẹ bi awọn 12CrMoV.Ati pe o tun le ṣee lo ni iwọn otutu ṣiṣẹ alurinmorin ni isalẹ 540 ℃, gẹgẹbi 15CrMo pearlite ooru sooro, irin.O tun le ṣee lo lati weld 30CrMnSi irin simẹnti.Pupọ julọ awọn ohun elo alurinmorin pẹlu awọn ibeere akoonu erogba kekere le ṣee lo si elekiturodu ọwọ irin ti o ni igbona.O tun jẹ olokiki pupọ ni ọja, ati awọn abajade esi ọja tun dara pupọ.A gba imọ-ẹrọ iṣelọpọ to ti ni ilọsiwaju, iṣakoso muna ni ipese ti awọn ohun elo aise, sisẹ ati iṣelọpọ, ayewo ọja, iṣẹ lẹhin-tita ti gbogbo alaye, lati pese awọn alabara pẹlu elekiturodu ti o dara julọ ati iṣẹ okun waya.
Awọn ẹya ara ẹrọ
AWS E8015-G iru ọwọ alurinmorin elekiturodu fun ooru sooro irin ni a kekere soda hydrogen iru ọwọ alurinmorin elekiturodu, pẹlu idurosinsin aaki, kere asesejade, ti o dara m, rorun desagging, o tayọ X-Ray išẹ, idurosinsin darí ini, le bojuto ga ikolu toughness. labẹ awọn ipo itọju ooru.Eleyi ọwọ elekiturodu ni a pearlite ooru sooro irin elekiturodu ti o ni awọn 0.5% molybdenum, 1% chromium, vanadium, awọn lilo ti DC yiyipada alurinmorin isẹ ti, le jẹ gbogbo ipo alurinmorin, nilo lati preheat to 250 ~ 300 ℃ ṣaaju ki o to alurinmorin.Itọju igbona lẹhin-alurinmorin yẹ ki o ṣe ni 730 ± 15 ℃ * 2h ni ibamu pẹlu awọn ibeere boṣewa ti awọn ohun elo alurinmorin.Ati ki o to alurinmorin, o jẹ pataki lati yọ epo, ipata, ọrinrin ati awọn miiran ise lori weldment.
Ile-iṣẹ & Ile-iṣẹ
Ọja tiwqn ati darí-ini ifihan
KỌMPUTA kemikali
ALOY(wt%) | C | Mn | Si | Cr | Mo | P | S | V |
GB/T OFIN | 0.05-0.12 | 0.90 | 0.60 | 0.80-1.50 | 0.40-0.65 | 0.03 | 0.030 | 0.10-0.35 |
Aws ofin | - | ≥1.00 | ≥0.80 | ≥0.30 | ≥0.20 | 0.04 | 0.030 | ≥0.10 |
APEERE IYE | 0.07 | 0.75 | 0.35 | 1.15 | 0.5 | 0.013 | 0.018 | 0.150 |
Ohun-ini ẹrọ:
ONÍNÌYÀN | AGBARA YIELD(MPa) | AGBARA Ifaagun (MPa) | ÌTẸ̀RẸ̀YÌN ℃xh | IMAPACT IYE J/℃ | ÌGBÀGBÀ(%) | |||||||||
GB/T OFIN | 460 | 550 | 730*2 | - | 15 | |||||||||
Aws ofin | 460 | 550 | 730*2 | - | 19 | |||||||||
APEERE IYE | 510 | 610 | 730*2 | 180 / Iseda otutu | 23 |
Niyanju welding PARAMETER:
DIAMETERS PIPICATIONS(mm) | 2.6*350 | 3.2*350 | 4.0 * 400 | 5.0 * 400 | ||||||
ELECTRICITY (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||||
O/W | 60-100 | 80-120 | 120-160 | - |
Awọn alaye Iṣakojọpọ:
ÌSÍPÍṢẸ́ | AGBO | PCS/1KG | ÌWÚN/1KG | |||
2.6mm | 300mm | 48PCS | 2KG | |||
3.2mm | 350mm | 27 PCS | 5KG | |||
4.0mm | 350mm | 16 PCS | 5KG | |||
5.0mm | 350mm | 12 PCS | 5KG |
Awọn ọran Aṣoju
Iwe-ẹri
Ọja tiwqn ati darí-ini ifihan
KỌMPUTA kemikali
ALOY(wt%) | C | Mn | Si | Cr | Mo | P | S | V |
GB/T OFIN | 0.05-0.12 | 0.90 | 0.60 | 0.80-1.50 | 0.40-0.65 | 0.03 | 0.030 | 0.10-0.35 |
Aws ofin | - | ≥1.00 | ≥0.80 | ≥0.30 | ≥0.20 | 0.04 | 0.030 | ≥0.10 |
APEERE IYE | 0.07 | 0.75 | 0.35 | 1.15 | 0.5 | 0.013 | 0.018 | 0.150 |
Ohun-ini ẹrọ:
ONÍNÌYÀN | AGBARA YIELD(MPa) | AGBARA Ifaagun (MPa) | ÌTẸ̀RẸ̀YÌN ℃xh | IMAPACT IYE J/℃ | ÌGBÀGBÀ(%) | |||||||||
GB/T OFIN | 460 | 550 | 730*2 | - | 15 | |||||||||
Aws ofin | 460 | 550 | 730*2 | - | 19 | |||||||||
APEERE IYE | 510 | 610 | 730*2 | 180 / Iseda otutu | 23 |
Niyanju welding PARAMETER:
DIAMETERS PIPICATIONS(mm) | 2.6*350 | 3.2*350 | 4.0 * 400 | 5.0 * 400 | ||||||
ELECTRICITY (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||||
O/W | 60-100 | 80-120 | 120-160 | - |
Awọn alaye Iṣakojọpọ:
ÌSÍPÍṢẸ́ | AGBO | PCS/1KG | ÌWÚN/1KG | |||
2.6mm | 300mm | 48PCS | 2KG | |||
3.2mm | 350mm | 27 PCS | 5KG | |||
4.0mm | 350mm | 16 PCS | 5KG | |||
5.0mm | 350mm | 12 PCS | 5KG |